It has many excellent characteristics, in the low-molecular curing does not produce any harmful substances, no pollution, absolutely non-toxic, then a large depth can be completely cured, to the environment and long-term use at about 280 ℃, excellent electrical performance particularly.
Use: for self-regulating PTC heating ceramics, its high temperature resistance, good thermal conductivity, it is used extensively for PTC replace imported products.
Instructions:
1、Use according to A: B = 1: 1 weight ratio weighed in a clean container, stir (be original device bonding site for general processing).
2、On the original device may also be applied to the adhesive screen printing.
Technical Specifications:
Nan da 283silicone | Nan da 284silicone | ||
solid Of before | Exterior | Red does not flow viscose body | Gray does not flow viscose body |
Viscosity (pa·s) | 100~300 | 100~300 | |
A、BRatio of the components(A:B) (g) | 1:1 | 1:1 | |
allows the operating time(h) | ≥24h/25℃ | ≥24h/25℃ | |
Curing conditions(heating) |
60~30min /180-200℃ |
60~30min /180-200℃ | |
solid Of Rear | tensile strength( Mpa≥) | 2.5 | 2.5 |
Elongation at break (%≥) | 160 | 160 | |
Shore hardness( A) | 25~55 | 25~55 | |
Volume resistivity( Ω·cm≥ ) | 2.3×10 13 | 2.3×10 14 | |
Permittivity(1MH Z≤) | 7.0 | 6.8 | |
Dielectric loss tangent(1MH Z ≤ ) | 4×10 -2 | 3×10 -2 | |
Breakdown strength(KV/mm≥) | 7 | 8 | |
Flammability rating (GB/T13488-1992) |
FV-0 UL94V-0 |
FV-0 UL94V-0 | |
Thermal conductivity( w/m·k≥) | 0.7 | 0.7 | |
density(g·cm 3 ) | 1.9 | 1.9 | |
Operating temperature(℃) | -50~300 | -50~300 |
Precautions:
1、Do not mix organic matter and organic tin impurities such as nitrogen, phosphorus, sulfur and other elements, in order to avoid curing bad.
2、A, B component and the tools used to be separate dedicated (cause agglomeration after mixed, so that plastic scrap).Storage conditions: keep in a cool, dry place, duration: one year.